- ホーム
- JIS G 0560:2008
- 規格番号
- JIS G 0560:2008
- 制定年
- 2008
- 出版団体
- Japanese Industrial Standards Committee (JISC)
- 最新版
-
JIS G 0560:2008
- 交換する
-
JIS G 0560:1998
- 範囲
- This Standard specifies the method of sulphur print for steel whose sulphur content
is normally 0.100 % or under. In the case where the sulphur content is over 0.100 %,
the test may be performed by diluting the etching solution.
This Standard is also applicable to steel castings.
NOTE 1 The International Standard corresponding to this Standard is as fol-
lows.
ISO 4968 : 1979 Steel- Macrographie examination by sulfur print
(Baumann method) (MOD)
In addition, symbols which denote the degree of correspondence in
the contents between the relevant International Standard and JIS are
IDT (identical), MOD (modified), and NEQ (not equivalent) according
to ISO/IEC Guide 21.
NOTE 2 The sulphur print is essentially a qualitative test. Because of this, it is
not advisable to assess the sulphur content of a given steel merely on
the basis of its sulphur print.
NOTE 3 Care shall be taken for the following cases because the appearance of
sulphur print may be altered.
a) For the steel containing titanium, the sulphur print may sometimes
be difficult to be appeared.
b) When testing the face subjected to cold working, the appearance of
sulphur print may be altered.
c) Depending on the sensitivity of photographic paper, the appearance
of sulphur print may be altered.
NOTE 4 As the application of test and the assessment of result vary depending
on the steel type, application and the like, they shall be specified ac-
cording to product standards for detail or subjected to the agreement
between the purchaser and the manufacturer.
JIS G 0560:2008 規範的参照
JIS G 0560:2008 発売履歴